FCWw-TMW11C

TUU 28.7-31749248.002-2002 (suspended) EN 14700/ T Fe9 DIN 8555/ (suspended) EN ISO 17632-A: Т CrNiMn15 U N 3 EN ISO 17632-B: Т Z 2 M21 3 AWS A5.20: ECrNiMn15T0-3 AWS A5.22: ECCrNiMn15

Welding process: S – under the flux	Wire diameter, mm	Recommended shielding gases and fluxes
S	3,0

General characteristics

Наплавка валков центрифуг линий производства минерального утеплителя

Weldability

The Formation of the weld bead	good
Separation of Slag	excellent
Deposition Rate, kg/h	5-18
Addiction Weld metal Cracking	low
Consumption per 1 kg of wire Weld metal, kg	1.05-1.25
Weld metal Hardness (HRC for 3rd-4th layer, unless otherwise stated)	after surfacing HB 520-HB 520

Recommended Flux Brand - АН-26

Recommended Surfacing Modes

Wire diameter, mm	Current, A	Voltage, V	Производительность Vн м/ч
3,0	280-300	30	24

Deposit composition (Weld metal), %

C	Si	Mn	Ni	Cr	S	P
0.07	0.7	6.8	9.5	19.0	≤0.012	≤0.03

_

Properties of the weld metal

Обеспечивает гарантированное бездефектное качество наплавленного металла. Наплавленный металл обладает высокой стойкостью к разгару, жаростойкостью и окалиностойкостью.
В процессе наплавки наблюдается самопроизвольное отделение шлаковой корки, малая волнистость гладкой поверхности наплавленного металла, отсутствие дефектов в виде пор, зашлаковок и трещин.

Technological features

Автоматическая наплавка выполняется по винтовой линии с 50% перекрытием проволокой.

Delivery type (More)

Wire diameter, mm	Cardboard barrel			Molded skeins of frameless type		Frame drum (B)	Coil (S), (BS)
				Hank in the corrugation box	Metallic barrel
	To 100 kg	To 150 kg	To 300 kg	To 30 kg	To 70 kg	To 25 kg	To 15 kg

---

Articles and website pages that mention this wire

There are no articles in this language