| Product name and permissible diameters | EN ISO, AWS | Typical mechanical properties of the weld metal | Purpose and scope. Deposit composition (Weld metal), % |
| TMW1 О - Ø1,0-2,8 | EN ISO 17632-А Т 35 A Z N3 EN ISO 17632-B T 43 A T6 NO | UTS~460...550 MPa YS~330MPa A5≥16% KCV+20°: 40J/cm2 | This self-shielding flux-cored wire is designed for mechanized arc welding of metal structures of general purpose low-carbon and low alloyed steels in flat position. The wire can be easily adopted for welding in the field conditions or when performing mounting and assembling works. [C: ≤0.12; Si: 0.2; Mn: ≤0.8; S: ≤0.035; P: ≤0.035; ] |
| TMW2 G - Ø1,6-2,0 | EN ISO 17632-A: T 42 0 R Cl 3 AWS A5.22(20,9): E710-1C | UTS~560 MPa YS~440MPa A5≥16% KCV+20°: ≥60J/cm2 KCV0°: ≥35J/cm2 | It is designed for gas shielded mechanied arc welding and cladding of welds of building metal structures, technological vessels and pipelines, parts and components of agricultural and railroad machines, hot-galvanization low-carbon steel tanks, machine building, transport and load-lifting machine engineering. [C: 0.09; Si: 0.1; Mn: 0.6; S: ≤0.03; P: ≤0.03; ] |
| TMW4 G - Ø1,2-2,4 | EN ISO 17632-A: T 42 2 R NO 3 EN ISO 17632-B: T 49 2 T5 0 NO | UTS~510 MPa YS~400MPa A5≥20% KCV+20°: ≥80J/cm2 KCV-20°: ≥35J/cm2 | Gas-shielding (G) flux-cored wire for mechanized arc welding, surfacing and filling-up patching of defects in metal structure castings made of low-carbon and low alloyed steels. [C: 0.1; Si: 0.2; Mn: 1.2; S: ≤0.03; P: ≤0.03; ] |
| TMW5mc G - Ø1,0–2,0 | EN ISO 17632-A: T 42 4 M M21 3 H 5 AWS A5.22(20,9): E70Tl 5-M21 A4-G-H4 | UTS~520 MPa YS~420MPa A5≥22% KCV+20°: ≥160J/cm2 KCV-20°: ≥100J/cm2 KCV-40°: ≥60J/cm2 | It is designed for high-speed single- or multi-pass automatic robotized arc welding of metal structures of carbon and low-alloyed steels as well as ship-building steels in flat position using shielding atmosphere of argon-based gas mixtures. [C: ≤0.1; Si: 0.45; Mn: 1.5; S: ≤0.02; P: ≤0.02; ] |
| TMW7 G - Ø1,2–2,4 | EN ISO 17632-A: T 42 4 Р С 1 Н5 EN ISO 17632-B: Т 42 2 P C1 H10 AWS A5.22(20,9): E71T1-C1A4-CS2-H4 AWS A5.22(20,9): E71T1-M21A4-CS2-H8 | UTS~490 MPa YS~400MPa A5≥22% KCV+20°: ≥120J/cm2 KCV-20°: ≥90J/cm2 KCV-40°: ≥70J/cm2 | Rutile all-positional welding flux-cored wire is designed for gas shielded arc welding of metal structures of low-carbon and low-alloyed steels, including the following: the shipbuilding steels of the D32 - E40 grades and rolled steel sheets of increased strength and plain steels of the S235 and S355 grades with heightened plasticity requirements to weld metal at low temperatures being set to. [C: ≤0.09; Si: 0.4; Mn: 1.3; S: ≤0.03; P: ≤0.03; ] |
| TMW8 G - Ø1,2–2,4 | EN ISO 17632-A: T 42 0 P Cl AWS A5.22(20,9): E71T-1C H4 AWS A5.22(20,9): E71T-1M H8 | UTS~500 MPa YS~400MPa A5≥20% KCV+20°: ≥50J/cm2 KCV-20°: ≥35J/cm2 KCV-30°: ≥50J/cm2 | It is designed for gas-shielded mechanized arc welding of metal structures made of low-carbon and low-alloyed steels, general purpose rolled steel sheets of increased strength with carbon content being less than 0.25 3 (wt.). [C: 0.12; Si: 0.3; Mn: 1.2; S: ≤0.035; P: ≤0.035; ] |
| TMW29 G - Ø1,2-3,6 | EN ISO 17632-A: T 42 3 R C1 | UTS~490 MPa YS~440MPa A5≥22% KCV+20°: ≥80J/cm2 KCV-40°: ≥35J/cm2 | It is designed for gas-shielded mechanized 1.2-3.6 mm arc welding of metal structures made of low-carbon and low-alloyed steels, rolled steel sheets of increased strength, including those exploited at low temperatures. It can be used for filling-up patching of flaws in the castings of carbon and alloyed structural steels. [C: 0.12; Si: 0.3; Mn: 1.4; S: ≤0.03; P: ≤0.03; ] |
| Product name and permissible diameters | EN ISO, AWS | Typical mechanical properties of the weld metal | Purpose and scope. Deposit composition (Weld metal), % |
| TMW3 О - Ø1,6-2,4 | EN ISO 17632-A: T 42 2 1NI Y NO 3 | UTS~490...660 MPa YS~400MPa A5≥20% KCV+20°: ≥80J/cm2 KCV-20°: ≥35J/cm2 | Self-shielding flux-cored wire is designed for mechanized arc welding of metal structures made of ordinary quality low-carbon steels and rolled steel sheets of increased strength at open-air sites. [C: ≤0.12; Si: 0.2; Mn: 1.2; Ni: 1.0; Al: 0.85; S: ≤0.02; P: ≤0.02; ] |
| TMW57 G - Ø1,2–2,4 | EN ISO 17632-A: T 55 4 Z R C1 EN ISO 17632-B: T 55 4 Z R M21 AWS A5.22(20,9): E91T1-C1A4-G-H4 | UTS~650...800 MPa YS~590MPa A5≥16% KCV0°: ≥100J/cm2 KCV-20°: ≥80J/cm2 KCV-40°: ≥60J/cm2 | It is designed for gas-shielded arc welding of heavy-duty metal structures made of low-alloyed high-strength steels, alloyed structural steels and other ones with yield strength not less than 580 MPa. [C: ≤0.12; Si: 0.3; Mn: 1.2; Cr: 0.3; Ni: 1.1; Mo: 0.3; S: ≤0.03; P: ≤0.03; ] |
| Product name and permissible diameters | EN ISO, AWS | Typical mechanical properties of the weld metal | Purpose and scope. Deposit composition (Weld metal), % |
| TMW14mc G - Ø1,2–3,6 | EN ISO 17632-A: T CrMo1 R С1 AWS A5.22(20,9): E81T1-B2-H4 | UTS~500 MPa YS~430MPa A5≥22% KCV+20°: ≥100J/cm2 KCV0°: ≥80J/cm2 KCV-20°: ≥50J/cm2 | It is designed for gas-shielded mechanized arc welding, surfacing and filling-up patching of flaws in steel castings and metal structures of high-alloyed and stainless steels, high-temperature and creep resistant steels and alloys which are exploited at temperature up to 545 °C. [C: 0.06; Si: 0.3; Mn: 0.8; Cr: 1.0; Mo: 0.5; S: ≤0.03; P: ≤0.03; ] |
| TMW15mc G - Ø1,2–3,6 | EN ISO 17632-A: T CrMo1 R С1 AWS A5.22(20,9): E81T1-B2-H4 | UTS~490 MPa YS~340MPa A5≥18% KCV+20°: ≥80J/cm2 KCV0°: ≥60J/cm2 KCV-20°: ≥40J/cm2 | It is designed for gas-shielded mechanized arc welding, surfacing and filling-up patching of flaws in steel castings and metal structures of high-alloyed and stainless steels, high-temperature and creep resistant steels and alloys which are exploited at temperature up to 545 °C. [C: 0.06; Si: 0.3; Mn: 0.8; Cr: 1.0; Mo: 0.5; V: 0.2; S: 0.014; P: 0.012; ] |
| Product name and permissible diameters | EN ISO, AWS | Typical mechanical properties of the weld metal | Purpose and scope. Deposit composition (Weld metal), % |
| WELTEC-H210Y О - Ø1,6–2,4 | EN ISO 17632-A: T ZR NO 3 (EN ISO 17632-А T Z R M21 3) (EN ISO 17632-А T Z R C1 3) AWS A5.22(20,9): EСrMnT0-3 AWS A5.22(20,9): ECCrMn20 | UTS~500...690 MPa YS~360MPa A5≥24% KCV+20°: ≥80J/cm2 KCV-20°: ≥60J/cm2 | It is for open-arc or gas-shielded mechanized arc welding of joints of pearlitic steels and high-manganese steels. [C: 0.15; Si: 0.2; Mn: 18.0; S: ≤0.02; P: ≤0.025; Ti: 0.1; Cr: 8.0; ] |
| TMW11 О - Ø2,0–3,0 | EN ISO 17632-A: T Z R NO 3 (EN ISO 17632-А T Z R M21 3) (EN ISO 17632-А T Z R C1 3) AWS A5.22(20,9): ECrNiMn15T0-3 AWS A5.22(20,9): ECCrNiMn15 | UTS~520 MPa YS~400MPa A5≥32% KCV+20°: ≥80J/cm2 KCV-20°: ≥50J/cm2 | It is designed for open-arc or gas-shielded mechanized arc welding of joints of low-carbon and low-alloyed steels as well as alloyed structural steels with austenitic steels. [C: 0.1; Si: 0.2; Mn: 13.0; Ni: 8.0; S: ≤0.02; P: ≤0.02; Cr: 9.0; ] |
| Product name and permissible diameters | EN ISO, AWS | Typical mechanical properties of the weld metal | Purpose and scope. Deposit composition (Weld metal), % |
| FCW-ASC2 О - Ø1,6-3,0 G - Ø1,6-3,0 | EN ISO 17632-A: T C FeC-2-N-3 AWS A5.22(20,9): ECI-B | UTS~160...200 MPa YS~350...410MPa A5≥-% | Предназначена для механизированной сварки или исправления дефектов литья из чугуна с пластинчатым графитом. [C: 4.0; Si: 3.2; Mn: 0.4; Ti: 0.9; Al: 0.5; S: 0.007; P: 0.016; ] |