| Product Name | Ultimate tensile strength, MPa | Yield Strength, MPa | Elongation (l = 5×d) | Charpy V-Notch, KCV, J/cm2 at T °C | Purpose and scope. Deposit composition (Weld metal), % |
| FCW-ASC2 T C FeC-2-N-3 ECI-B О - Ø1,6-3,0 G - Ø1,6-3,0 2019.12.27 (✅) | 160-200 | 350-410 | - | Предназначена для механизированной сварки или исправления дефектов литья из чугуна с пластинчатым графитом. [C: 4.0; Si: 3.2; Mn: 0.4; Ti: 0.9; Al: 0.5; S: 0.007; P: 0.016; ] |
| Product Name | Ultimate tensile strength, MPa | Yield Strength, MPa | Elongation (l = 5×d) | Charpy V-Notch, KCV, J/cm2 at T °C | Purpose and scope. Deposit composition (Weld metal), % |
| TMW3 T 42 2 1NI Y NO 3 О - Ø1,6-2,4 2023.12.07 (✅) | 490-660 | 400 | 20 | +20°: ≥80; -20°: ≥35 | Self-shielding flux-cored wire is designed for mechanized arc welding of metal structures made of ordinary quality low-carbon steels and rolled steel sheets of increased strength at open-air sites. [C: ≤0.12; Si: 0.2; Mn: 1.2; Ni: 1.0; Al: 0.85; S: ≤0.02; P: ≤0.02; ] |
| TMW57 T 55 4 Z R C1 E91T1-C1A4-G-H4 G - Ø1,2–2,4 2023.12.07 (✅) | 650-800 | 590 | 16 | 0°: ≥100; -20°: ≥80; -40°: ≥60 | It is designed for gas-shielded arc welding of heavy-duty metal structures made of low-alloyed high-strength steels, alloyed structural steels and other ones with yield strength not less than 580 MPa. [C: ≤0.12; Si: 0.3; Mn: 1.2; Cr: 0.3; Ni: 1.1; Mo: 0.3; S: ≤0.03; P: ≤0.03; ] |
| Product Name | Ultimate tensile strength, MPa | Yield Strength, MPa | Elongation (l = 5×d) | Charpy V-Notch, KCV, J/cm2 at T °C | Purpose and scope. Deposit composition (Weld metal), % |
| WELTEC-H210Y T ZR NO 3 EСrMnT0-3 О - Ø1,6–2,4 2023.12.08 (✅) | 500-690 | 360 | 24 | +20°: ≥80; -20°: ≥60 | It is for open-arc or gas-shielded mechanized arc welding of joints of pearlitic steels and high-manganese steels. [C: 0.15; Si: 0.2; Mn: 18.0; S: ≤0.02; P: ≤0.025; Ti: 0.1; Cr: 8.0; ] |
| TMW11 T Z R NO 3 ECrNiMn15T0-3 О - Ø2,0–3,0 2023.12.08 (✅) | 520 | 400 | 32 | +20°: ≥80; -20°: ≥50; : | It is designed for open-arc or gas-shielded mechanized arc welding of joints of low-carbon and low-alloyed steels as well as alloyed structural steels with austenitic steels. [C: 0.1; Si: 0.2; Mn: 13.0; Ni: 8.0; S: ≤0.02; P: ≤0.02; Cr: 9.0; ] |
| Product Name | Ultimate tensile strength, MPa | Yield Strength, MPa | Elongation (l = 5×d) | Charpy V-Notch, KCV, J/cm2 at T °C | Purpose and scope. Deposit composition (Weld metal), % |
| TMW1 Т 35 A Z N3 О - Ø1,0-2,8 2023.10.28 (✅) | 460-550 | 330 | 16 | +20°: 40 | This self-shielding flux-cored wire is designed for mechanized arc welding of metal structures of general purpose low-carbon and low alloyed steels in flat position. The wire can be easily adopted for welding in the field conditions or when performing mounting and assembling works. [C: ≤0.12; Si: 0.2; Mn: ≤0.8; S: ≤0.035; P: ≤0.035; ] |
| TMW2 T 42 0 R Cl 3 E710-1C G - Ø1,6-2,0 2023.12.04 (✅) | 560 | 440 | 16 | +20°: ≥60; 0°: ≥35 | It is designed for gas shielded mechanied arc welding and cladding of welds of building metal structures, technological vessels and pipelines, parts and components of agricultural and railroad machines, hot-galvanization low-carbon steel tanks, machine building, transport and load-lifting machine engineering. [C: 0.09; Si: 0.1; Mn: 0.6; S: ≤0.03; P: ≤0.03; ] |
| TMW4 T 42 2 R NO 3 G - Ø1,2-2,4 2023.12.06 (✅) | 510 | 400 | 20 | +20°: ≥80; -20°: ≥35 | Gas-shielding (G) flux-cored wire for mechanized arc welding, surfacing and filling-up patching of defects in metal structure castings made of low-carbon and low alloyed steels. [C: 0.1; Si: 0.2; Mn: 1.2; S: ≤0.03; P: ≤0.03; ] |
| TMW5mc T 42 4 M M21 3 H 5 E70Tl 5-M21 A4-G-H4 G - Ø1,0–2,0 2023.12.06 (✅) | 520 | 420 | 22 | +20°: ≥160; -20°: ≥100; -40°: ≥60 | It is designed for high-speed single- or multi-pass automatic robotized arc welding of metal structures of carbon and low-alloyed steels as well as ship-building steels in flat position using shielding atmosphere of argon-based gas mixtures. [C: ≤0.1; Si: 0.45; Mn: 1.5; S: ≤0.02; P: ≤0.02; ] |
| TMW7 T 42 4 Р С 1 Н5 E71T1-C1A4-CS2-H4 G - Ø1,2–2,4 2023.12.06 (✅) | 490 | 400 | 22 | +20°: ≥120; -20°: ≥90; -40°: ≥70 | Rutile all-positional welding flux-cored wire is designed for gas shielded arc welding of metal structures of low-carbon and low-alloyed steels, including the following: the shipbuilding steels of the D32 - E40 grades and rolled steel sheets of increased strength and plain steels of the S235 and S355 grades with heightened plasticity requirements to weld metal at low temperatures being set to. [C: ≤0.09; Si: 0.4; Mn: 1.3; S: ≤0.03; P: ≤0.03; ] |
| TMW8 T 42 0 P Cl E71T-1C H4 G - Ø1,2–2,4 2023.12.06 (✅) | 500 | 400 | 20 | +20°: ≥50; -20°: ≥35; -30°: ≥50 | It is designed for gas-shielded mechanized arc welding of metal structures made of low-carbon and low-alloyed steels, general purpose rolled steel sheets of increased strength with carbon content being less than 0.25 3 (wt.). [C: 0.12; Si: 0.3; Mn: 1.2; S: ≤0.035; P: ≤0.035; ] |
| TMW29 T 42 3 R C1 G - Ø1,2-3,6 2023.12.06 (✅) | 490 | 440 | 22 | +20°: ≥80; -40°: ≥35 | It is designed for gas-shielded mechanized 1.2-3.6 mm arc welding of metal structures made of low-carbon and low-alloyed steels, rolled steel sheets of increased strength, including those exploited at low temperatures. It can be used for filling-up patching of flaws in the castings of carbon and alloyed structural steels. [C: 0.12; Si: 0.3; Mn: 1.4; S: ≤0.03; P: ≤0.03; ] |