| Product name, conditions of use, type of protection and permissible diameters | EN 14 700 DIN 8555 | Weld metal Hardness (HRC for 3rd-4th layer, unless otherwise stated) | Purpose and scope. Deposit composition (Weld metal), % |
| WT-H250 О - Ø1,6-3,0 G - Ø1,2-2,4 S - Ø1,6-3,2 
| T Fe1 MF 1-GF-250-P | after surfacing HB 200-HB 280 | It is designed for automatic as well as semi-automatic open-arc or gas-shielded arc or submerged arc restoration and hard-facing of parts made of carbon and low-alloyed steels operating under conditions of metal-to-metal friction at room and elevated temperatures. [C: 0.08; Mn: 0.8; Si: 0.5; Ti: 0.4; S: 0.012; P: 0.017; ] |
| WT-H290 О - Ø1,6-3,0 G - Ø1,2-2,4 S - Ø1,6-3,6 
| T Fe1 MF 1-GF-250-P | after surfacing HB 220-HB 340 | It is designed for automatic as well as semi-automatic open-arc or gas-shielded arc or submerged arc restoration and hard-facing of parts made of carbon and low-alloyed steels operating under conditions of metal-to-metal friction at room and elevated temperatures. [C: 0.1; Mn: 0.6; Si: 0.5; Cr: 0.5; Ni: 0.3; Mo: 0.5; S: 0.012; P: 0.017; ] |
| WELTEC-H290-RM2 О - Ø1,6-3,0 G - Ø1,2-2,4 S - Ø1,6-3,6
| T Fe1 MF 1-GF-250-P | after surfacing HB 220-HB 340 | Порошковая проволока марки ВЕЛТЕК-Н290-РМ2-O предназначена для автоматической и полуавтоматической наплавки открытой дугой при восстановлении и упрочнении деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при нормальных и повышенных температурах. Рекомендуется для наплавки на постоянном токе обратной полярности. [C: 0.1; Mn: 1.2; Si: 0.7; Cr: 2.5; S: 0.012; P: 0.017; ] |
| WT-H350 G - Ø1,2-2,4 S - Ø1,6-3,6
| T Fe1 MF 1-GF-350-P | after surfacing 32-42 | It is designed for automatic as well as semi-automatic submerged arc cladding of parts operating under conditions of metal-to-metal sliding and rolling friction. [C: 0.2; Mn: 1.2; Si: 0.8; Cr: 1.1; Mo: 0.4; S: 0.016; P: 0.015; ] |
| WT-H370 G - Ø1,2-2,4 S - Ø1,6-3,6
| T Fe3 MF 1-GF-350-GP | after surfacing 32-42 | It is designed for automatic and semi-automatic open-arc or gas-shielded arc or submerged arc restoration and hard-facing of parts made of carbon and low-alloyed steels operating under conditions of metal-to-metal friction at room and elevated temperatures. [C: 0.15; Mn: 0.6; Si: 0.8; Cr: 3.0; Mo: 1.2; V: 0.4; S: 0.012; P: 0.017; ] |
| WELTEC-H370-RMK G - Ø1,2-2,4 S - Ø1,6-5,0
| T Z Fe3 MF 1-GF-350-GP | after surfacing 30-42 | Порошковая проволока марки ВЕЛТЕК-Н370-РМК предназначена для автоматической и полуавтоматической под слоем флюса и в защитных газах при восстановлении и упрочнении деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при нормальных и повышенных температурах. Рекомендуется для наплавки на постоянном токе обратной полярности. [C: 0.15; Mn: 1.4; Si: 0.8; Cr: 3.0; Mo: 1.2; V: 0.4; S: 0.012; P: 0.017; ] |
| WELTEC-H370-02 G - Ø1,2-2,4 S - Ø1,6-3,6
| T Z Fe3 MF 1-GF-350-GP | after surfacing 30-42 | Порошковая проволока марки ВЕЛТЕК-Н370.02 предназначена для автоматической и полуавтоматической наплавки под флюсом и в среде защитных газов при восстановлении и упрочнении деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при нормальных и повышенных температурах.Рекомендуется для наплавки на постоянном токе обратной полярности. [C: 0.1; Mn: 1.5; Si: 0.6; Cr: 4.0; S: 0.018; P: 0.017; ] |
| WT-H371 G - Ø1,2-2,4 S - Ø1,6-3,6
| T Fe3 MF 1-GF-250-P | after surfacing 35-40 | It is designed for automatic as well as semi-automatic gas-shielded arc or submerged arc cladding. [C: 0.1; Mn: 1.5; Si: 0.6; Cr: 3.0; S: 0.018; P: 0.017; ] |
| Wet-FCW-Sw-14MnSiTi О - Ø1,6–3,0
| after surfacing HB 230-HB 280 | Порошковая проволока марки ВеТ ПП-Нп-14ГСТ предназначена для автоматической и полуавтоматической наплавки открытой дугой на детали из углеродистых конструкционных сталей и литых сталей марок 25Л и 45Л, работающих в условиях трения металла о металл. Рекомендуется для наплавки на постоянном токе обратной полярности.. [C: 0.14; Mn: 0.5; Si: 0.5; Ti: 0.4; S: 0.03; P: 0.03; ] | |
| FCW-Sw-12Cr12Mn12SiV S - Ø1,6–3,6 
| after surfacing HB 200-HB 240 after work hardening 40-50 | Порошковая проволока марки ПП-Нп-12Х12Г12СФ предназначена для автоматической и наплавки под флюсом деталей, работающих в трения и коррозии. Рекомендуется для наплавки на постоянном токе обратной полярности. [C: 0.1; Cr: 13.5; Mo: 13.5; Si: 0.8; V: 1.0; B: 0.05; N: 0.12; S: 0.03; P: 0.03; ] | |
| FCW-Sw-14MnSiTi О - Ø1,6–3,0
| T Fe 1 MF 1-GF-250-P | after surfacing HB 220-HB 280 | Порошковая проволока марки ПП-Нп-14ГСТ предназначена для автоматической и полуавтоматической наплавки открытой дугой на детали из углеродистых конструкционных сталей и литых сталей марок 25Л и 45Л, работающих в условиях трения металла о металл. Рекомендуется для наплавки на постоянном токе обратной полярности. [C: 0.08; Mn: 0.6; Si: 0.5; Ti: 0.4; S: 0.012; P: 0.017; ] |
| FCW-Sw-18Cr1Mn1Mo Ø1,6–3,6
| after surfacing HB 280-HB 380 | Порошковая проволока марки ПП-Нп-18Х1Г1М предназначена для автоматической и полуавтоматической наплавки под флюсом и в среде защитных газов износостойкого слоя на детали, работающие в условиях трения металла о металл и абразивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности. [C: 0.17; Cr: 1.5; Mn: 1.5; Si: <0.8; Mo: 0.5; W: 1.2; S: 0.04; P: 0.06; ] | |
| FCW-Sw-19MnSiTi О - Ø1,6–3,0
| after surfacing HB 260-HB 320 | Порошковая проволока марки ПП-Нп-19ГСТ предназначена для автоматической и полуавтоматической наплавки открытой дугой деталей из углеродистых сталей, работающих в условиях трения металла о металл. Рекомендуется для наплавки на постоянном токе обратной полярности. [C: 0.19; Cr: 0.35; Mn: 0.5; Si: 0.6; Ti: 0.6; S: 0.03; P: 0.03; ] |